Composition for aqueous coating material and process for its production, and two-component curable aqueous coating material kit

ABSTRACT

A composition for aqueous coating material which has a low content of an organic solvent and presents little burden on the environment and which is excellent in storage stability. 
     A composition for aqueous coating material, which comprises a synthetic resin containing a fluorinated copolymer (A) comprising from 40 to 60 mol % of a fluoro-olefin unit, from 3 to 50 mol % of an alkyl vinyl ether or alkyl vinyl ester unit, from 4 to 30 mol % of a hydroxyl group-containing vinyl ether unit and 0.4 to 7 mol % of a structural unit of the following formula (a4):

TECHNICAL FIELD

The present invention relates to a composition for aqueous coatingmaterial containing a crosslinkable fluorinated copolymer and a processfor its production, and a two-component curable aqueous coating materialkit.

BACKGROUND ART

In recent years, for protection of natural environment, environmentalpollution such as photochemical smog or global warming due to dischargeof organic solvents, has been taken up as a problem, and dischargeregulation or emission control is being implemented. Particularly inEurope, such control is advanced, and also in Japan, Air PollutionControl Law was revised in 2006, and legal discharge regulations wereimplemented.

In order to meet such legal regulations, also in the field of coatingmaterials, efforts have been made to develop a coating method toincrease the coating efficiency to effectively utilize a coatingmaterial or to introduce a high solid type coating material byincreasing the solid content in a coating material thereby to reduce asolvent to be discharged. However, with such a high solid type coatingmaterial, there is a limit in reduction of the solvent.

Heretofore, compositions for aqueous coating materials have been knownwherein various synthetic resins of e.g. alkyd type, acryl type,polyester type, polyvinyl acetate type or epoxy type, are dispersed ordissolved in water. An aqueous coating composition employing acrosslinkable fluorinated copolymer having hydroxyl groups, as such asynthetic resin or as a part of such a synthetic resin, is widely known,since it is excellent in weather resistance.

As a fluorinated copolymer to be used for a composition for aqueouscoating material, one having some of hydroxyl groups esterified tointroduce carboxyl groups in an organic solvent and further having someor all of such carboxyl groups neutralized by a basic compound, in orderto increase the affinity to water, is known (Patent Document 1).

Further, a fluorinated copolymer obtained by emulsion polymerization isalso known (Patent Document 2). However, in the aqueous dispersion oraqueous solution of the fluorinated copolymer in Patent Document 1, alarge amount of an organic solvent used in the step of introducingcarboxyl groups will remain. Further, if the remaining organic solventis removed, the storage stability tends to deteriorate, andsedimentation tends to take place as the time passes.

On the other hand, in a case where a fluorinated copolymer obtained byemulsion polymerization is used as in Patent Document 2, an emulsioncoating material having a low solvent concentration can be obtained.However, the emulsion coating material has had a problem that thefilm-forming property is poor, or due to the remaining emulsifier, thewater resistance or adhesion tends to be poor.

Patent Document 1: JP-B-1-29488

Patent Document 2: Japanese Patent No. 3,356,803

DISCLOSURE OF THE INVENTION Object to be Accomplished by the Invention

The present invention has been made under the above-mentionedcircumstances and is to provide a composition for aqueous coatingmaterial containing a crosslinkable fluorinated copolymer, which isexcellent in storage stability even when the content of an organicsolvent is low. Further, it is to provide a process for producing such acomposition for aqueous coating material and a two-component curableaqueous coating material kit.

Means to Accomplish the Object

In order to accomplish the above object, the present invention providesthe following:

(1) A composition for aqueous coating material, which comprises waterand a synthetic resin dispersed or dissolved therein, wherein thesynthetic resin contains a fluorinated copolymer (A) comprising from 40to 60 mol % of a structural unit of the formula (a1), from 3 to 50 mol %of a structural unit of the formula (a2), from 4 to 30 mol % of astructural unit of the formula (a3) and 0.4 to 7 mol % of a structuralunit of the formula (a4) (provided that the total mol % value of therespective structural units of the formulae (a1), (a2), (a3) and (a4) isfrom 80 to 100); and which contains no solvent or a solvent in an amountof at most 10 mass % in the total mass of the composition for aqueouscoating material:

—CFX¹—CX²X³—  Formula (a1)

(provided that in the formula (a1), each of X¹ and X² which areindependent of each other, is a hydrogen atom, a chlorine atom or afluorine atom, and X³ is a chlorine atom, a fluorine atom or —CY¹Y²Y³,wherein each of Y¹, Y² and Y³ which are independent of one another, is ahydrogen atom, a chlorine atom or a fluorine atom);

(provided that in the formula (a2), R^(a) is a hydrogen atom or a methylgroup, R¹ is a C₁₋₁₂ alkyl group or a C₄₋₁₀ monovalent alicyclic group,j is an integer of from 0 to 8, and k is 0 or 1);

(provided that in the formula (a3), R^(b) is a hydrogen atom or a methylgroup, R² is a C₁₋₁₀ alkylene group or a C₄₋₁₀ bivalent alicyclic group,m is an integer of from 0 to 8, and n is 0 or 1); and

(provided that in the formula (a4), R^(b) and R² are as defined in theformula (a3), respectively, R³ is a C₂₋₁₀ alkylene group or a C₄₋₁₀bivalent alicyclic group, R⁴ is a hydrogen atom or —NHZ¹Z²Z³, whereineach of Z¹, Z² and Z³ which are independent of one another, is ahydrogen atom, a C₁₋₄ alkyl group or a C₁₋₆ hydroxyalkyl group, providedthat at least a part of R⁴ is required to be —NHZ¹Z²Z³, p is an integerof from 0 to 8, and q is 0 or 1).

(2) A process for producing a composition for aqueous coating material,which comprises:

an esterification step of reacting a fluorinated copolymer (B)comprising from 40 to 60 mol % of a structural unit of the formula (a1),from 3 to 50 mol % of a structural unit of the formula (a2) and from 4.4to 37 mol % of a structural unit of the formula (a3) (provided that thetotal mol % value of the respective structural units of the formulae(a1), (a2) and (a3) is from 80 to 100) with a dibasic acid anhydride inan organic solvent to esterify a part of the hydroxyl group in thestructural unit of the formula (a3) to introduce a carboxyl group;

a neutralizing step of adding a basic compound to neutralize at least apart of the carboxyl group with the basic compound;

a step of adding water; and

a step of removing the organic solvent:

—CFX¹—CX²X³—  Formula (a1)

(provided that in the formula (a1), each of X¹ and X² which areindependent of each other, is a hydrogen atom, a chlorine atom or afluorine atom, and X³ is a chlorine atom, a fluorine atom or —CY¹Y²Y³,wherein each of Y¹, Y² and Y³ which are independent of one another, is ahydrogen atom, a chlorine atom or a fluorine atom);

(provided that in the formula (a2), R^(a) is a hydrogen atom or a methylgroup, R¹ is a C₁₋₁₂ alkyl group or a C₄₋₁₀ monovalent alicyclic group,j is an integer of from 0 to 8, and k is 0 or 1); and

(provided that in the formula (a3), R^(b) is a hydrogen atom or a methylgroup, R² is a C₁₋₁₀ alkylene group or a C₄₋₁₀ bivalent alicyclic group,m is an integer of from 0 to 8, and n is 0 or 1).

(3) The process for producing a composition for aqueous coating materialaccording to the above (2), wherein the neutralizing step and the stepof adding water are conducted at the same time by adding an aqueoussolution of the basic compound.

(4) A two-component curable aqueous coating material kit which comprisesthe composition for aqueous coating material as defined in the above (1)and a water-soluble is or water-dispersible curing agent.

(5) The composition for aqueous coating material according to the above(1), wherein the structural unit of the formula (a2) is a structuralunit wherein j=k=0, and the structural unit of the formula (a3) is astructural unit wherein m=n=0.

(6) The composition for aqueous coating material according to the above(1) or (5), wherein the organic solvent is at least one member selectedfrom the group consisting of alcohols, cellosolves, propylene glycolderivatives and ketones.

(7) The composition for aqueous coating material according to the above(1), (5) or (6), which contains the organic solvent in an amount of atmost 3 mass % in the total mass of the composition for aqueous coatingmaterial.

(8) The composition for aqueous coating material according to the above(1), (5), (6) or (7), wherein the content of the structural unit of theformula (a4) in the fluorinated copolymer is from 1.4 to 6 mol %.

(9) The two-component curable aqueous coating material kit according tothe above (4), wherein the water-soluble or water-dispersible curingagent is an isocyanate compound.

(10) The two-component curable aqueous coating material kit according tothe above (4), wherein the water-soluble or water-dispersible curingagent is a non-blocked isocyanate.

EFFECTS OF THE INVENTION

The composition for aqueous coating material of the present inventionhas a low content of an organic solvent and presents little burden onthe environment. Further, in spite of the low content of an organicsolvent, it is excellent in storage stability.

Further, by the process for producing a composition for aqueous coatingmaterial of the present invention, it is possible to produce acomposition for aqueous coating material which has a low content of anorganic solvent and presents little burden on the environment and whichis excellent in storage stability.

Further, the two-component curable aqueous coating material kit of thepresent invention employs the composition for aqueous coating materialexcellent in storage stability in spite of the low content of an organicsolvent, and thus, it presents little burden on the environment and isexcellent in the handling efficiency.

BEST MODE FOR CARRYING OUT THE INVENTION Composition for Aqueous CoatingMaterial Fluorinated Copolymer A

The composition for aqueous coating material of the present invention isan aqueous coating composition having a synthetic resin dispersed ordissolved in water, wherein the synthetic resin contains a fluorinatedcopolymer (A).

The fluorinated copolymer (A) comprises a structural unit of the formula(a1), a structural unit of the formula (a2), a structural unit of theformula (a3) and a structural unit of the formula (a4). The total mol %value of the respective structural units of the formulae (a1), (a2),(a3) and (a4) is from 80 to 100, preferably from 95 to 100.

Further, in the present specification, the structural unit of theformula (a1) may also be shown as “a structural unit (a1).” The sameapplies to compounds represented by other formulae.

The structural unit (a1) is a structural unit of the following formula(a1) derived from a fluoroolefin type compound.

—CFX¹—CX²X³—  (a1)

Further, in the formula (a1), each of X¹ and X² which are independent ofeach other, is a hydrogen atom, a chlorine atom or a fluorine atom, andX³ is a chlorine atom, a fluorine atom or —CY¹Y²Y³, (wherein each of Y¹,Y² and Y³ which are independent of one another, is a hydrogen atom, achlorine atom or a fluorine atom).

As the structural unit (a1), it is possible to mention a structural unitderived from the following fluoroolefin type compound:

A fluoroethylene such as CF₂═CF₂, CClF═CF₂, CHCl═CF₂, CCl₂═CF₂,CClF═CClF, CHF═CCl₂, CH₂═CClF or CCl₂═CClF; a fluoropropene such asCF₂ClCF═CF₂, CF₃CCl═CF₂, CF₃CF═CFCl, CF₂ClCCl═CF₂, CF₂ClCF═CFCl,CFCl₂CF═CF₂, CF₃CCl═CClF, CF₃CCl═CCl₂, CClF₂CF═CCl₂, CCl₃CF═CF₂,CF₂ClCCl═CCl₂, CFCl₂CCl═CCl₂, CF₃CF═CHCl, CClF₂CF═CHCl, CH₃CCl═CHCl,CHF₂CCl═CCl₂, CF₂ClCH═CCl₂, CF₂ClCCl═CHCl, CCl₃CF═CHCl or CH₂BrCF═CCl₂;or a fluoroolefin type compound having at least 4 carbon atoms such asCF₃CCl═CFCF₃, CF₂═CFCF₂CClF₂ or CF₃CF₂CF═CCl₂.

Among them, CF₂═CF₂ or CClF═CF₂ is preferred since the weatherresistance of a coated film is excellent.

The content of the structural unit (a1) in the fluorinated copolymer (A)is from 40 to 60 mol %, preferably from 45 to 55 mol %.

When the content of the structural unit (a1) is in the above range, thesufficient weather resistance will be obtained, and the glass transitiontemperature of a polymer will not be too high, whereby it is possible toobtain an amorphous good film.

The structural unit (a2) is a structural unit of the following formula(a2) derived from e.g. an alkyl vinyl ether, alkyl vinyl ester, alkylallyl ether or alkyl allyl ester.

Here, in the formula (a2), R^(a) is a hydrogen atom or a methyl group,R¹ is a C₁₋₁₂ alkyl group or a C₄₋₁₀ monovalent alicyclic group, j is aninteger of from 0 to 8, and k is 0 or 1.

The structural unit of the formula (a2) is preferably an alkyl vinylether or alkyl vinyl ester, wherein j=0, and k=0 or 1.

The structural unit (a2) may, for example, be a structural unit derivedfrom ethyl vinyl ether, n-butyl vinyl ether, cyclohexyl vinyl ether,vinyl acetate, vinyl valerate or vinyl pivalate, and among them, astructural unit is properly selected depending upon the desired coatedfilm physical properties (hardness, gloss, pigment dispersibility,etc.).

Among them, a structural unit derived from ethyl vinyl ether orcyclohexyl vinyl ether is preferred since the alternatingcopolymerizability with the structural unit (a1) is good, and it is easyto adjust the glass transition temperature of the resin.

The content of the structural unit (a2) is from 3 to 50 mol %,preferably from 20 to 45 mol %, based on the total structural units ofthe fluorinated copolymer (A). In the present invention, it is possibleto use two or more types of the structural unit (a2).

The structural unit (a3) is a structural unit of the following formula(a3) derived from a hydroxyl group-containing vinyl ether, a hydroxylgroup-containing vinyl ester, a hydroxyl group-containing allyl ether ora hydroxyl group-containing allyl ester.

Here, in the formula (a3), R^(b) is a hydrogen atom or a methyl group,R² is a C₁₋₁₀ alkylene group or a C₄₋₁₀ bivalent alicyclic group, m isan integer of from 0 to 8, and n is 0 or 1.

The structural unit (a3) may, for example, be a structural unit derivedfrom 2-hydroxyalkyl vinyl ether, 4-hydroxybutyl vinyl ether,1-hydroxymethyl-4-vinyloxy methylcyclohexane or 4-hydroxybutyl vinylester, and among them, a structural unit derived from a hydroxyalkylvinyl ether is preferred from the viewpoint of polymerizability,crosslinking property, etc.

The content of the structural unit (a3) in the fluorinated copolymer (A)is from 4 to 30 mol %, preferably from 8 to 25 mol %.

If the content of the structural unit (a3) is too small, the crosslinkdensity will be low when a crosslinking reaction is carried out.Further, if the content of the structural unit (a3) is too large, thereis a concern that the water resistance of a coated film will decrease.

The structural unit (a4) is a structural unit of the following formula(a4).

Here, in the formula (a4), R^(b) and R² are as defined in the formula(a3), respectively, R³ is a C₂₋₁₀ alkylene group or a C₄₋₁₀ bivalentalicyclic group, R⁴ is a hydrogen atom or —NHZ¹Z²Z³, wherein each of Z¹,Z² and Z³ which are independent of one another, is a hydrogen atom, aC₁₋₄ alkyl group or a C₁₋₆ hydroxyalkyl group, provided that at least apart of R⁴ is required to be —NHZ¹Z²Z³, p is an integer of from 0 to 8,and q is 0 or 1.

In the structural unit (a4), the proportion of R⁴ being —NHZ¹Z²Z³ ispreferably from 30 to 100 mol %, more preferably from 50 to 100 mol %.

The content of the structural unit (a4) in the fluorinated copolymer (A)is from 0.4 to 7 mol %, preferably from 1.4 to 6 mol %.

When the content of the structural unit (a4) is in the above range, thesolubility or dispersibility in water will be excellent, and thestability in water will be excellent.

The fluorinated copolymer (A) in the present invention may contain atmost 20 mol % of a structural unit (hereinafter referred to as anotherstructural unit) other than the structural units (a1), (a2), (a3) and(a4).

Such another structural unit may, for example, be a structural unitderived from an ethylenic monomer.

The particularly preferred structure of the fluorinated copolymer (A) isa structure comprising from 45 to 55 mol % of the structural unit (a1),from 14 to 45.6 mol % of the structural unit (a2), from 8 to 25 mol % ofthe structural unit (a3), from 1.4 to 6 mol % of the structural unit(a4) and no another structural unit.

Another Synthetic Resin Component

In the composition for aqueous coating material of the presentinvention, a synthetic resin other than the fluorinated copolymer (A)may be dispersed or dissolved in water together with the fluorinatedcopolymer (A). Such another synthetic resin may be a synthetic resin ofe.g. a fluorine type, a phenol type, an alkyd type, a melamine type, aurea type, a vinyl type, an epoxy type, a polyester type, a polyurethanetype or an acryl type.

The fluorine type synthetic resin may, for example, be a fluorinatedcopolymer having, as essential structural components, polymerized unitsderived from fluoroolefin described in Japanese Patent No. 2955336 andpolymerized units derived from a macromonomer having a hydrophilicmoiety. Here, the hydrophilic moiety means a moiety having a hydrophilicgroup, a moiety having a hydrophilic bond or a moiety made of acombination thereof. Further, the macromonomer is a polymer or oligomerhaving a low molecular weight and having a radical polymerizableunsaturated group on its one end. When such a fluorinated copolymer iscontained in the composition, the mechanical stability and chemicalstability of the aqueous coating material composition will be improved,such being preferred.

In the composition for aqueous coating material of the presentinvention, the proportion of the fluorinated copolymer (A) in thesynthetic resin dispersed or dissolved in water is preferably from 10 to95 mass %, more preferably from 50 to 90 mass %.

When other than the fluorine type synthetic resin is used as thesynthetic resin other than the fluorinated copolymer (A), it ispreferred to adjust the proportion of the fluorinated copolymer (A) tobe at least 55 mass % from a viewpoint such that excellent weatherresistance will be imparted.

In the composition for aqueous coating material of the presentinvention, the solid content concentration of the synthetic resindispersed or dissolved in water is preferably from 3 to 50 mass %, morepreferably from 30 to 50 mass %.

The composition for aqueous coating material of the present inventionmay be one which does not contain an organic solvent or one whichcontains at most 10 mass %, preferably at most 3 mass %, of the organicsolvent in the total mass of the composition for aqueous coatingmaterial.

As the organic solvent which may possibly be contained, it is possibleto mention, for example, a residue of an organic solvent used for theesterification step which will be described hereinafter. Further, it isalso possible to mention a residue of an organic solvent used for thepolymerization step of a fluorinated copolymer (B) which will bedescribed hereinafter.

The composition for aqueous coating material of the present inventionpreferably optionally contains an additive such as a coalescer, aleveling additive, a thickener, an ultraviolet absorber, a lightstabilizer or an antifoaming agent.

The coalescer may, for example, be diethylene glycol monoethyl etheracetate, 2,2,4-trimethyl-1,3-pentane diol mono(2-methylpropionate) ordiethylene glycol diethyl ether.

The coalescer is one type of the organic solvent in the presentinvention. Therefore, when the coalescer is incorporated, the sum of thecontents of the coalescer and other organic solvents is adjusted to beat most 10 mass % in the composition for aqueous coating material.

When the coalescer is incorporated, its content is preferably at most 3parts by mass, particularly preferably at most 1 part by mass, per 100parts by mass of the synthetic resin (the solid content of the polymer).

The leveling additive may, for example, be preferably apolyether-modified polydimethylsiloxane or a polyether-modifiedsiloxane.

The thickener may, for example, be preferably a polyurethane typeassociative thickener.

As the ultraviolet absorber, it is possible to use various known ones.Particularly, the ultraviolet absorber suitably for use as a transparentcoating material for top coating may, for example, be a salicylate suchas methyl salicylate, phenyl salicylate, cresyl salicylate or benzylsalicylate; a benzophenone such as 2-hydroxybenzophenone,2-hydroxy-4-benzyloxy benzophenone, 2-hydroxy-4-octoxy benzophenone,2-hydroxy-5-chlorobenzophenone, 2-aminobenzophenone or a high molecularweight-modified product sold as T-57 manufactured by Adeka corporation;a benzotriazole such as 2-(2′-hydroxy-5′-t-butylphenyl)benzotriazole,2-(2′-hydroxy-5′-t-butylphenyl)-5-chlorobenzotriazole,2-(2′-hydroxy-5′-methoxyphenyl)benzotriazole,2-(2′-hydroxy-3′,5′-di-neopentylphenyl)benzotriazole or a high molecularweight-modified product sold as TINUVIN 900 or 1130 manufactured byNihon Ciba-Geigy K.K.; a substituted acronitrile such as ethyl2-cyano-3,3-diphenylacrylate, 2-ethylhexyl 2-cyano-3,3-diphenylacrylateor methyl α-cyano-β-methyl-4-methoxycinnamate; a nickel complex saltsuch as 2,2′-thiobis(4-octylphenolate) nickel complex salt or[2,2′-thiobis(4-t-octylphenolate)]-n-butylamine-nickel complex salt; anultraviolet absorber such as dimethyl p-methoxybenzylidene malonate,resorcinol monobenzoic acid ester, hexamethylphosphoric triamide or2,5-diphenyl-p-benzoquinone;bis(2,2,6,6-tetramethyl-4-piperidine)sebacate and dimethylsuccinate/1-(2-hydroxyethyl)-4-hydroxy-2,2,6,6-tetramethylpiperidinepolycondensate, or bis(1,2,2,6,6-pentamethyl-4-piperizyl)2-(3,5-di-t-butyl-4-hydroxybenzyl)-2-n-butylmalonate. They may be usedalone or in combination as mixture of two or more of them.

It is preferred to use the ultraviolet absorber in an amount of from 0.1to 15 parts by mass, particularly preferably from 0.1 to 5 parts bymass, per 100 parts by mass of the solid content concentration of thesynthetic resin. If the amount of the ultraviolet absorber is too small,its effect of improving the weather resistance cannot be sufficientlyobtained, and if it is too large, its effect is saturated, such beingnot proper.

The light stabilizer may, for example, be a hindered amine type lightstabilizer such as MARK LA 57, 62, 63, 67 or 68, manufactured by Adekacorporation or TINUVIN 622LD manufactured by Nihon Ciba-Geigy K.K. Theymay be used alone or as a mixture of two or more of them in combinationwith the ultraviolet absorber.

The antifoaming agent may, for example, be a fatty acid salt, a higheralcohol sulfate, a liquid fatty oil sulfuric acid ester, an aliphaticamine or aliphatic amide sulfate, an aliphatic alcohol phosphoric acidester, a sulfonate of dibasic fatty acid ester, a fatty acid amidesulfonate, an alkyl allyl sulfonate, a naphthalene sulfonate offormaline condensate, a polyoxyethylene alkyl ether, a polyoxyethylenealkyl phenol ether, a polyoxyethylene alkyl ester, a sorbitan alkylester, a polyoxyethylene sorbitan alkyl ester, an acrylic polymer, asilicone mixed acrylic polymer, a vinyl polymer or a polysiloxanecompound.

The antifoaming effect is influenced by the balance (HLB value) betweenhydrophilic groups and hydrophobic groups, and among such antifoamingagents, one having HLB of at most 6, particularly preferably at most 4is preferably used.

Further, if it is necessary to adjust the gloss of the coated film, acommonly used inorganic or organic delustering agent may simply beadded.

Further, if coloring is needed, a coloring material such as acommercially available organic pigment, inorganic pigment, organic dye,or a pigment or dye obtained by complexing them, may be dispersed, oradded and mixed.

Process for Producing Composition for Aqueous Coating Material

A process for producing a composition for aqueous coating material ofthe present invention comprises an esterification step of reacting afluorinated copolymer (B) with a dibasic acid anhydride in an organicsolvent to esterify a part of the hydroxyl group in the structural unitof the formula (a3) to introduce a carboxyl group, a neutralizing stepof adding a basic compound to neutralize at least a part of the carboxylgroup with the basic compound, a step of adding water, and asolvent-removing step of removing the organic solvent.

Fluorinated Copolymer (B)

A fluorinated copolymer (B) comprises from 40 to 60 mol % of thestructural unit (a1), from 3 to 50 mol % of the structural unit (a2) andfrom 4.4 to 37 mol % of the structural unit (a3) (provided that thetotal mol % value of the respective structural units of the formulae(a1), (a2) and (a3) is from 80 to 100).

The mol % of the structural unit (a3) in the fluorinated copolymer (B)is equal to the total mol % of the structural units (a3) and (a4) in thefluorinated copolymer (A) contained in the composition for aqueouscoating material of the present invention.

It is possible to produce the fluorinated copolymer (B) bycopolymerizing a monomer of the formula (b1), a monomer of the formula(b2) and a monomer of the formula (b3), as shown below (hereinaftersometimes referred to as “a monomer (b1)” or the like) under an alkalinecondition in the presence or absence of a polymerization catalyst, byapplying a polymerization initiating source such as a polymerizationinitiator or an ionizing radiation. In order to maintain thecopolymerization reaction system in an alkaline side, thecopolymerization reaction is carried out in the presence of a basiccompound.

The monomer (b1) is a compound of the following formula (b1).

CFX¹═CX²X³  Formula (b1)

Here, in the formula (b1), each of X¹ and X² means the same as in theabove formula (a1).

The monomer (b2) is a monomer of the following formula (b2).

Here, in the formula (b2), each of R^(a), R¹, j and k means the same asin the above formula (a2).

The monomer (b3) is a compound of the following formula (b3).

Here, in the formula (b3), each of R^(b), R², m and n means the same asin the above formula (a3).

The changing proportions (mol %) of the monomer (b1), monomer (b2) andmonomer (b3) are the same as the mol % of the structural unit (a1),structural unit (a2) and structural unit (a3), respectively, whichconstitute the fluorinated copolymer (B).

As the polymerization initiator, a peroxy ester type peroxide such ast-butylperoxyacetate, a dialkylperoxy dicarbonate such as diisopropylperoxy dicarbonate, benzoyl peroxide, or azobisisobutylonitrile, may,for example, be used.

The amount of the polymerization initiator to be used may suitably bechanged depending on the type or copolymerization reaction conditions,but usually, it is used in an amount of from about 0.05 to 0.5 mass %based on the total amount of monomers to be copolymerized.

The amount of the basic compound to be used is from about 0.01 to 20mass %, preferably from about 0.1 to 10 mass %, based on the totalamount of monomers need to be copolymerized.

Further, the basic compound to be present during the polymerization canbe selected from a wide range of organic basic compounds and inorganicbasic compounds. The organic basic compound is preferably an alkylaminesuch as triethylamine or an alkylphosphine such as triethylphosphine.The inorganic basic compound is preferably a carbonate, hydroxide oroxide of an alkali metal or an alkaline earth metal such as potassiumcarbonate, potassium hydroxide, sodium hydroxide or magnesium hydroxide.

For the above copolymerization reaction, it is preferred to use solutionpolymerization. As a solvent, it is preferred to use an alcohol, anester, a ketone, a saturated halogenated hydrocarbon containing at leastone fluorine atom or an aromatic hydrocarbon such as xylene.

The reaction temperature for the copolymerization reaction is preferablyfrom 10° C. to 90° C. Further, the reaction pressure is preferably from0 to 100 kg/cm²·G, more preferably from 1 to 50 kg/cm²·G.

The fluorinated copolymer (B) preferably has the intrinsic viscosity offrom 0.05 to 2.0 dL/g. By using a reaction solvent having a relativelylarge chain transfer constant, or by carrying out the reaction in thecoexistence of a suitable chain transfer agent, it is possible tosuppress the intrinsic viscosity within the above range.

The number average molecular weight of the fluorinated copolymer (B) ispreferably in a range of from 3,000 to 200,000. If the molecular weightis less than 3,000, the weather resistance of a coated film willsometimes decrease. If the molecular weight is beyond 200,000, coatingproperty will decrease, and a coated film appearance will sometimesdeteriorate.

Esterification Step

In the esterification step, a dibasic acid anhydride is reacted with thefluorinated copolymer (B) in an organic solvent to esterify a part ofthe hydroxyl group in the structural unit of (a3) to introduce acarboxyl group.

As the dibasic acid anhydride, e.g. succinic anhydride, glutaricanhydride, itaconic anhydride, adipic anhydride, 1,2-cyclohexanedicarboxylic anhydride, cis-4-cyclohexene-1,2-dicarboxylic anhydride,phthalic anhydride, 1,8-naphthalic anhydride or maleic anhydride ispreferably used.

The organic solvent may, for example, be an alcohol such as methanol,ethanol, n-propanol, isopropanol, n-butanol, isobutanol, secondarybutanol, tertiary butanol or pentanol; a cellosolve such as methylcellosolve, ethyl cellosolve, isopropyl cellosolve, butyl cellosolve orsecondary butyl cellosolve; a propylene glycol derivative such aspropylene glycol methyl ether, dipropylene glycol methyl ether orpropylene glycol methyl ether acetate; ethylene glycol ethyl etheracetate; a ketone such as acetone, methyl ethyl ketone or methylisobutyl ketone; or an aromatic compound such as toluene or xylene. Itis properly selected by taking solubilities of the fluorinated copolymer(B) and dibasic acid anhydride, etc. into consideration.

Further, if the organic solvent used in the polymerization step forproducing the fluorinated copolymer (B) is sufficiently remained, it isnot necessary to add an organic solvent additionally in theesterification step.

In the esterification step, it is possible to use a catalyst incombination. As the catalyst, a carboxylic acid metal salt, an alkalihydroxide, an alkali metal carbonate, a quaternary ammonium salt or atertiary amine may be used, but a tertiary amine such as triethylamineis preferred.

The esterification step is carried out at a reaction temperature ofpreferably from room temperature to 150° C., more preferably from 50 to100° C. The reaction time is from several tens minutes to several hours.

The amount of the dibasic acid anhydride to be reacted is determined byadjusting it so that the content of the structural unit (a4) will befrom 0.4 to 7 mol % and the content of the structure (a3) will be from 4to 30 mol % in a fluorinated copolymer (A) to be eventually obtained.

The amount of the structural unit (a4) after the esterification reactioncan be ascertained by measuring an acid number. When the acid numberafter the esterification reaction is from 2 to 35 mgKOH/g, it ispossible to ascertain that the structural unit (a4) is in an amount offrom 0.4 to 7 mol %.

The amount of the structural unit (a3) before the esterificationreaction can be ascertained by a hydroxyl group value before theesterification. In order to have the structural unit (a3) in an amountof from 4 to 30 mol %, it is necessary to have a hydroxyl group value offrom 20 to 150 mgKOH/g before the esterification, and an acid number tobe in the above range after the esterification.

Neutralizing Step

In the neutralizing step, the basic compound is added to the esterifiedfluorinated copolymer (B) to neutralize at least a part of the carboxylgroup introduced in the esterification step with the basic compound. Inthe structural unit (a4), the proportion to be neutralized with thebasic compound is preferably from 30 to 100 mol %, more preferably from50 to 100 mol %.

The reaction in the neutralizing step sufficiently proceeds when thebasic compound or an aqueous solution of the basic compound is added toan organic solvent wherein the esterified fluorinated copolymer (B) isdissolved, at room temperature with stirring for several tens minutes.

In the neutralizing step, water is added together with the basiccompound to the organic solvent wherein the esterified fluorinatedcopolymer (B) is dissolved. Water can be added simultaneously with thebasic compound or separately, and some of it can be addedsimultaneously, and the rest of it can be added separately. When some orall of the water is added simultaneously, it is preferably added as anaqueous solution of the basic compound. When it is added separately, itcan be added before or after adding the basic compound.

Among them, a method of adding water after adding the basic compound anda method of adding an aqueous solution of the basic compound arepreferred.

The amount of water to be added in the neutralizing step is preferablyadjusted so that the solid content concentration of the esterifiedfluorinated copolymer (B) becomes from 3 to 50 mass %, particularly from15 to 35 mass %.

The basic compound to be used in the neutralizing step preferably has aboiling point of at most 200° C. so that the basic compound will hardlyremain in a coated film.

The basic compound may, for example, be ammonia; a primary, secondary ortertiary alkylamine such as monomethylamine, dimethylamine,trimethylamine, monoethylamine, diethylamine, triethylamine,monoisopropylamine, diisopropylamine, triisopropylamine, monobutylamineor dibutylamine; an alkanolamine such as monoethanolamine,monoisopropanolamine, dimethylaminoethanol or diethylaminoethanol; adiamine such as ethylene diamine, propylene diamine, tetramethylenediamine or hexamethylene diamine; an alkylene imine such as ethyleneimine or propylene imine; piperazine, morpholine, pyrazine or pyridine.

Step of Removing Solvent

In the step of removing the solvent, the organic solvent is removed.Consequently, it is possible to obtain an aqueous coating materialcomposition wherein the organic solvent is at most 10 mass % based onthe total mass.

Here, as the solvent to be removed, a residue of an organic solvent usedfor the esterification step, may be mentioned. Further, a residue of anorganic solvent used in the polymerization step for producing thefluorinated copolymer (B), may also be mentioned.

The solvent can be removed by distillation under reduced pressure.

Two-Component Curable Aqueous Coating Material Kit

The two-component curable aqueous coating material kit of the presentinvention comprises the composition for aqueous coating material of thepresent invention and a curing agent. The composition of aqueous coatingmaterial of the present invention is one to be used as mixed with thecuring agent. Depending on the curing agent, crosslinking is possibleeven by drying at room temperature, and it is possible to form a coatedfilm by applying the composition of aqueous coating material and thecuring agent. When heating is needed for crosslinking, a coated film maybe formed by heating and baking.

The curing agent is a water-soluble or water dispersible curing agenthaving a functional group reactive with a hydroxyl group or carboxylgroup.

The curing agent may, for example, be an isocyanate type compound, amelamine resin, a phenol resin, a xylene resin or a toluene resin.Particularly, an isocyanate type compound is preferred since it ispossible to easily obtain a coated film excellent in weather resistanceand mechanical property.

The isocyanate type compound is preferably one mechanically dispersed inwater or a self-emulsifiable polyisocyanate compound. Theself-emulsifiable polyisocyanate compound is a compound which is capableof being emulsified and dispersed in water without an emulsifier.

The polyisocyanate compound to be mechanically dispersed in water may,for example, be an aliphatic polyisocyanate such as hexamethylenediisocyanate; an aromatic polyisocyanate such as m- or p-phenylenediisocyanate, 2,4- or 2,6-tolylene diisocyanate,diphenylmethane-4,4′-diisocyanate, naphthalene-1,5-diisocyanate or4,4′-diisocyanate-3,3′-dimethyldiphenyl; an alicyclic polyisocyanatesuch as bis-(isocyanate cyclohexyl)methane or isophorone diisocyanate; acrude polyisocyanate such as crude tolylene diisocyanate or crudediphenylmethane diisocyanate; or a modified polyisocyanate such ascarbodiimide-modified diphenylmethane diisocyanate, polyol-modifieddiphenylmethane diisocyanate or polyol-modified hexamethylenediisocyanate.

Such a polyisocyanate may be a dimer or trimer depending on its typesuch as a Burette type, an isocyanurate ring type or uretdione type, orit may be a blocked polyisocyanate obtained by reacting an isocyanategroup with a block agent.

The block agent may, for example, be an alcohol, a phenol, acaprolactam, an oxime or an active methylene compound.

The above polyisocyanates may be used in combination as a mixture of twoor more of them.

As the polyisocyanate, one mechanically dispersed in water is used.

The polyisocyanate to be mechanically dispersed in water is preferablyone having a relatively low viscosity.

If an emulsifier is added during the dispersion, more stable dispersioncan be obtained. As the emulsifier to be used here, a known one may beused without any particular limitation, but it is not preferred to useone having an ionic, particularly, active hydrogen atom since itundergoes a reaction during the dispersion to increase the viscosity ordeteriorate the dispersibility. A non-ionic emulsifier, particularly anemulsifier having a polyoxyethylene chain is preferred.

A blocked polyisocyanate does not usually become cured unless it isheated at a temperature of at least 140° C. Therefore, when curing isdesired to be carried out at a temperature lower than such atemperature, it is preferred to use a non-blocked polyisocyanate.

Further, as the self-emulsifiable polyisocyanate compound, it ispossible to exemplify a prepolymer obtained by reacting the abovepolyisocyanate with a hydrophilic polyoxyalkylene.

The hydrophilic polyoxyalkylene is preferably one having at least oneisocyanate reactive group and a number average molecular weight in arange of from 200 to 4,000. Particularly preferred is a polyoxyalkylenepolyol or polyoxyalkylene monool having a molecular weight in a range offrom 300 to 1,500. One having a low molecular weight cannot sufficientlyachieve its self-emulsifying property. One having a high molecularweight has a good self-emulsifying property, but its stability in waterbecomes poor, and its crystallinity becomes high, whereby the storagestability at a low temperature will decrease, and turbidity will becaused.

The oxyalkylene chain in the polyoxyalkylene is preferably one made ofentirely or mostly an oxyethylene group from the viewpoint ofhydrophilicity.

The reaction of the polyisocyanate with the polyoxyalkylene glycol iscarried out in the presence of a catalyst such as a tertiary amine, analkyl-substituted ethylene imine, a tertiary alkyl phosphine, a metalalkyl acetonate or an organic acid metal salt, and as the case requires,in the presence of a promoter at a temperature of at most 100° C.Further, with respect to the reaction, it is preferred to adjust theamount of remaining isocyanate group to be from 10 to 24 mass %,particularly from 15 to 20 mass %.

If the amount of the remaining isocyanate group is small, the reactivitywith the fluorinated copolymer (A) will decrease, such being notpreferred. Further, in order to achieve sufficient crosslinking degree,a large amount of the isocyanate compound is needed, which is notpreferred since the weather resistance of a coated film will sometimesbe adversely affected. If the amount of the remaining isocyanate groupis too large, it is difficult to form a stable emulsion, such being notpreferred.

The self-emulsifiable isocyanate compound is described in e.g.JP-B-4-15270.

The melamine resin may, for example, be a melamine resin subjected to analkyl etherification such as methyl etherification, butyl etherificationor isobutyl etherification. From the viewpoint of water solubility, amelamine resin wherein at least a part of it is methyl-etherified, ispreferred.

The mass ratio of the composition for aqueous coating material to thecuring agent in the two-component curable aqueous coating material kitis 50 to 95 mass %/5 to 50 mass %, particularly preferably 65 to 90 mass%/10 to 35 mass %, by a compositional ratio of nonvolatile contents(based on the solid content of the polymer).

EXAMPLES

Now, the present invention will be described in further detail, but itshould be understood that the present invention is by no meansrestricted thereto.

In Examples, “parts” represents “parts by mass” unless otherwisespecified.

Evaluation of Storage Stability of Composition for Aqueous CoatingMaterial

Each of aqueous liquids in Synthetic Examples 1 to 5 wherein afluorinated copolymer is dispersed or dissolved in water, was prepared.Further, a synthetic resin dispersed of dissolved in the aqueous liquidof each of Synthetic Examples 1 to 3, corresponds to the fluorinatedcopolymer (A) of the present invention. Further, a synthetic resindispersed or dissolved in the aqueous liquid of each of SyntheticExamples 4 and 5, is a fluorinated copolymer different in the ratio ofstructural units from the fluorinated copolymer (A) of the presentinvention.

Synthetic Example 1

As the fluorinated copolymer (B), a fluororesin LUMIFLON flake(chlorotrifluoroethylene/ethyl vinyl ether/cyclohexyl vinylether/hydroxybutyl vinyl ether (mol % ratio: 50/15/15/20), hydroxylgroup value: 100 mgKOH/g, Mw: 7,000) for a coating material manufacturedby Asahi Glass Company, Limited, was dissolved in methyl ethyl ketone(MEK) to obtain a varnish having a solid content of 60 mass %.

To 300 parts of such varnish, 19.3 parts of a 20 mass % succinicanhydride acetone solution and 0.072 part of triethylamine as a catalystwere added, followed by a reaction at 70° C. for 6 hours foresterification. The infrared absorption spectrum of the reaction liquidwas measured, whereby the characteristic absorptions (1,850 cm⁻¹ and1,780 cm⁻¹) by an acid anhydride observed before the reaction were foundto have disappeared, and absorptions of carboxylic acid (1,710 cm⁻¹) andester (1,735 cm⁻¹) were observed. The acid number of the fluorinatedcopolymer after the esterification was 12 mgKOH/g, and the hydroxylgroup value was 86 mgKOH/g. According to such values of the acid numberand hydroxyl group value, about 2.4 mol % was esterified out of 20 mol %of hydroxybutyl vinyl ether structural units.

Then, to the esterified fluorinated copolymer, 2.73 parts oftriethylamine was added, followed by stirring at room temperature for 20minutes to neutralize a part of the carboxylic acid, and then 180 partsof deionized water was gradually added. As a result, about 1.7 mol % wasneutralized out of about 2.4 mol % of esterified structural units havingthe carboxyl group introduced.

After that, acetone and methyl ethyl ketone were distilled off underreduced pressure. Further, about 90 parts of deionized water was addedto obtain an aqueous liquid of Synthetic Example 1 having a solidcontent concentration of 40 mass %. The obtained raw materialcomposition in Synthetic Example 1, the acid number and hydroxyl groupvalue after the esterification, and mol % of each structural unitobtained from such values are shown in Table 1.

Further, in Table 1, (a1) represents mol % of chlorotrifluoroethylenestructural units, (a2) the total mol % of ethyl vinyl ether structuralunits and cyclohexyl vinyl ether structural units, (a3) mol % ofhydroxybutyl vinyl ether structural units, (a4-1) mol % ofnon-neutralized ones among esterified hydroxybutyl vinyl etherstructural units, and (a4-2) mol % of neutralized ones among esterifiedhydroxybutyl vinyl ether structural units.

Synthetic Examples 2 to 5

Each of aqueous liquids of Synthetic Examples 2 to 5 was obtained in thesame manner as in Synthetic Example 1 except that the amount of theacetone solution of succinic anhydride used for the esterification andthe amount of triethylamine used for the neutralizing reaction werechanged as shown in Table 1. In each of the obtained aqueous liquids ofSynthetic Examples 2 to 5, the raw material composition (parts by mass),the acid number and hydroxyl group value after the esterification of thesynthetic resin, and mol % of each structural unit obtained from suchvalues are shown in Table 1.

TABLE 1 Synthetic Synthetic Synthetic Synthetic Synthetic Unit Example 1Example 2 Example 3 Example 4 Example 5 Fluorinated Parts by 300 300 300300 300 copolymer mass varnish Succinic Parts by 19.3 33.8 48.2 65.993.2 anhydride mass Acid number mgKOH/g 12 21 30 41 58 Hydroxyl groupmgKOH/g 86 79 69 59 40 value Triethylamine Parts by 2.73 4.78 6.83 9.313.2 mass (a1) mol % 50 50 50 50 50 (a2) mol % 30 30 30 30 30 (a3) mol %17.6 15.8 14 11.8 8.4 (a4-1) mol % 0.7 1.3 1.8 2.5 3.5 (a4-2) mol % 1.72.9 4.2 5.7 8.1

Examples 1 to 3, Comparative Examples 1 and 2

To 100 parts by mass of each of aqueous liquids of Synthetic Examples 1to 5, components shown in Table 2 were added. Then, it was kept in anoven at 50° C. for 2 weeks, and the storage stability was checked. Theresults are shown in Table 2. Further, the names of the respectiveadditives in Table 2 represent the following compounds, respectively.Further, the numerical values in Table 2 are represented by parts bymass unless otherwise specified.

DEA: diethylene glycol monoethyl ether acetate

BYK348: a leveling additive (polyether-modified polydimethylsiloxane)manufactured by BYK-Chemie

BYK080: an antifoaming agent (silicon type antifoaming agent)manufactured by BYK-Chemie

TINUVIN 1130: An ultraviolet absorber (condensate ofmethyl-3-(3-t-butyl-5-(2H-benzotriazol-2-yl)-4-hydroxyphenyl)propionateand polyethylene glycol (molecular weight of 300)) manufactured by NihonCiba-Geigy K.K.

Sanor LS765: a light stabilizer manufactured by Sankyo Co., Ltd.

TABLE 2 Comp. Comp. Ex. 1 Ex. 2 Ex. 3 Ex. 1 Ex. 2 Aqueous Syn. Syn. Syn.Syn. Syn. liquid Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Acetone 0 0 5 0 15 DEA1.5 1.5 1.5 1.5 1.5 BYK348 0.5 0.5 0.5 0.5 0.5 BYK080 1 1 1 1 1 Sanor0.5 0.5 0.5 0.5 0.5 LS765 TINUVIN 3 3 3 3 3 1130 Organic 0% 0% 4.50% 0%12.30% solvent Storage No No No Sedimen- Sedimen- stability changechange change tation tation

As shown in Table 2, in Examples 1 to 3 wherein the aqueous liquids ofSynthetic Examples 1 to 3 were used, respectively, no change wasobserved although it was kept in an oven at 50° C. for 2 weeks, andthus, it was possible to confirm that the storage stability wasexcellent.

On the other hand, in Comparative Example 1 wherein the aqueous liquidof Synthetic Example 4 was used and no organic solvent was contained,sedimentation was observed.

In Comparative Example 2 wherein the aqueous liquid of Synthetic Example5 was used, sedimentation was observed even though the amount of anorganic solvent was 12.3%.

Evaluating Water Resistance of Coated Film Examples 4 to 6

To 100 parts by mass of each of the aqueous liquids of the SyntheticExamples 1 to 3, components shown in Table 3 were added. Then, each ofsuch liquids was spray-coated on a specimen which was obtained byapplying an acrylic type emulsion base coating material on a slateplate, and the specimen was dried at room temperature for 2 weeks.Further, the names of the respective additives in Table 3 represent thesame compounds in Table 2 except for ones shown below. Further, thenumerical values in Table 3 are represented by parts by mass unlessotherwise specified.

Bayhydur 3100: a water dispersible type polyisocyanate, manufactured bySumika Bayer Urethane Co., Ltd.

Water Resistance

Each of specimens of Examples 4 to 6 was immersed in deionized water atroom temperature for 2 weeks, and its appearance change was observed.The results are shown in Table 3.

Water Permeability

With respect to each of specimens of Examples 4 to 6, water permeabilitywas measured by a method described in JIS K5400. The results are shownin Table 3.

TABLE 3 Ex. 4 Ex. 5 Ex. 6 Synthetic Syn. Ex. 1 Syn. Ex. 2 Syn. Ex. 3Examples Acetone 0 0 5 DEA 1.5 1.5 1.5 Bayhydur 3100 15.2 14 12.2 BYK3480.5 0.5 0.5 BYK080 1 1 1 Sanor LS765 0.5 0.5 0.5 TINUVIN 1130 3 3 3Organic 0% 0% 4.50% solvent Water No change No change No changeresistance Water 0.08 0.08 0.1 permeability

As shown in Table 3, in Examples 4 to 6 wherein the aqueous liquids ofSynthetic Examples 1 to 3 were used, no change was observed in the waterresistance tests, and water permeability was very little. Therefore, itwas thus confirmed that by the two-component curable aqueous coatingmaterial kit of the present invention, it is possible to form a coatedfilm excellent in water resistance.

Evaluating Glossiness and Weather Resistance of Coated Film SyntheticExample 6

In 192.9 parts of deionized water, 20.0 parts of an emulsifier NEWCOL707NF manufactured by Nippon Nyukazai Co., Ltd., 204 parts of2-ethylhexyl acrylate, 195.8 parts of styrene and 8.2 parts of acrylicacid were added and emulsified by using a homomixer. Into the mixture,2.04 parts of ammonium persulfate was added, followed by pressurizationby nitrogen gas in a glass container and then by degassing to obtainliquid D.

On the other hand, into 1 L a stirrer-equipped glass reactor, 200 partsof deionized water was introduced, followed by pressurization bynitrogen gas and thereby degassing, whereupon the temperature was raisedto 80° C. Then, by using a tubular pump, 623.24 parts of liquid D wasdropped over a period of 3.5 hours. After that, 1 part of an aqueoussolution containing 10 mass % of ammonium persulfate was added thereto,followed by aging for 2.5 hours at a temperature of from 80 to 85° C.Then, it was cooled down to at most 30° C. and neutralized with a 28mass % aqueous ammonia to obtain an aqueous liquid of Synthetic Example6 having a solid content concentration of 50 mass %.

Preparation of Pigment Dispersion E

60 parts of titanium oxide pigment CR-90 (manufactured by IshiharaSangyo Kaisha, Ltd.), 2.9 parts of Disrol H-14N dispersant (manufacturedby Nippon Nyukazai Co., Ltd.), 0.2 part of FS antifoam 013B antifoamingagent (manufactured by Dow Corning Corporation), 38 parts of deionizedwater and 100 parts of glass beads were mixed, and by using a grain milldisperser, the mixture was dispersed, followed by removing the glassbeads by filtration to prepare the pigment dispersion E.

Example 7

100 Parts by mass of the aqueous liquid of Synthetic Example 1, 50 partsby mass of the aqueous liquid of Synthetic Example 6, 40 parts by massof the pigment dispersion E, 1.5 parts by mass of a coalescer DEA, 20.5parts by mass of a curing agent Bayhydur 3100 and 0.1 part by mass of apolyurethane type associative thickener BERMODOL PUR 2150 manufacturedby AKZO Nobel were blended and applied on an aluminum plate (thicknessof 1 mm and the surface is chromate treated) by using a film applicatorso that a film thickness as dried would be 40 μm, followed by baking at150° C. for 20 minutes to obtain a specimen. With respect to theappearance of such a specimen, the 600 gloss was 84. By using QUV tester(UC-1 type, QUV-B lamp, manufactured by Electric Devices), when theweather resistance was checked for 1,000 hours with a cycle ofirradiation time for 8 hours at 70 degree and wetting time for 4 hoursat 50 degree, the gloss retention was 98%, and the weather resistancewas thus confirmed to be good.

In Example 7 wherein the aqueous liquid of Synthetic Example 1 was usedin combination with other synthetic resins, the glossiness and weatherresistance were excellent. Therefore, it was confirmed that by thetwo-component curable aqueous coating material kit of the presentinvention, it is possible to form a coated film excellent in glossinessand weather resistance.

Synthetic Example 7

Into a stainless stirrer-equipped autoclave having an inner volume of200 mL, 19 parts of ethyl vinyl ether, 2 parts of cyclohexyl vinylether, 3 parts of hydroxybutyl vinyl ether, 4.5 parts of a macromonomer(EOVE) having a hydrophilic moiety, 60 parts of deionized water, 5 partsof an emulsifier NL-2320 manufactured by Nippon Nyukazai Co., Ltd., 0.35part of potassium carbonate and 0.1 part of ammonium persulfate wereintroduced, followed by cooling with ice, pressurizing with nitrogen gasuntil 3.5 kg/cm², and then degassing. After repeating such pressurizingand degassing twice, the mixture was degassed until 10 mmHg to removethe dissolved gas, and then, 38 parts of chlorotrifluoroethylene wasintroduced, followed by a reaction at 50° C. for 24 hours. At thecompletion of the reaction, the remaining gas was purged to obtain awater dispersion of the fluorinated copolymer.

Further, EOVE is a compound of the following formula, and it has anumber average molecular weight of about 500.

CH₂═CHOCH₂CH₂CH₂CH₂(OCH₂CH₂)_(r)OH

(wherein r is a positive integer)

Example 8

100 Parts by mass of the aqueous liquid of Synthetic Example 1, 50 partsby mass of the aqueous liquid of Synthetic Example 7, 40 parts by massof the pigment dispersion E, 3 parts by mass of a coalescer DEA, 20.5parts by mass of a curing agent Bayhydur 3100 and 0.1 part by mass of apolyurethane type associative thickener BERMODOL PUR 2150 manufacturedby AKZO Nobel were blended and applied on an aluminum plate (thicknessof 1 mm and the surface is chromate treated) by using a film applicatorso that a film thickness as dried would be 40 μm, followed by baking at150° C. for 20 minutes to obtain a specimen. With respect to theappearance of such a specimen, the 60° gloss was 82, and the weatherresistance for 1,000 hours by QUV test had little change, such beingpreferred.

As shown in Example 8, in Example 8 wherein the aqueous liquid ofSynthetic Example 1 was used in combination with the aqueous dispersionof other fluorinated copolymers, the glossiness and weather resistancewere excellent. Therefore, it was confirmed that by the two-componentcurable aqueous coating material kit of the present invention, it ispossible to form a coated film excellent in the glossiness and weatherresistance.

INDUSTRIAL APPLICABILITY

According to the process for producing a composition for aqueous coatingmaterial of the present invention, it is possible to produce acomposition for aqueous coating material which has a low content of anorganic solvent and presents little burden on the environment, and whichis excellent in storage stability. Further, the composition for aqueouscoating material is applicable as a two-component curable aqueouscoating material kit which presents little burden on the environment andexcellent handling efficiency.

The entire disclosures of Japanese Patent Application No. 2006-120464filed on Apr. 25, 2006 and Japanese Patent Application No. 2007-027081filed on Feb. 6, 2007 including specifications, claims and summaries areincorporated herein by reference in their entireties.

1. A composition for aqueous coating material, which comprises water anda synthetic resin dispersed or dissolved therein, wherein the syntheticresin contains a fluorinated copolymer (A) comprising from 40 to 60 mol% of a structural unit of the formula (a1), from 3 to 50 mol % of astructural unit of the formula (a2), from 4 to 30 mol % of a structuralunit of the formula (a3) and 0.4 to 7 mol % of a structural unit of theformula (a4) (provided that the total mol % value of the respectivestructural units of the formulae (a1), (a2), (a3) and (a4) is from 80 to100); and which contains no solvent or a solvent in an amount of at most10 mass % in the total mass of the composition for aqueous coatingmaterial:—CFX¹—CX²X³—  Formula (a1) (provided that in the formula (a1), each ofX¹ and X² which are independent of each other, is a hydrogen atom, achlorine atom or a fluorine atom, and X³ is a chlorine atom, a fluorineatom or —CY¹Y²Y³, wherein each of Y¹, Y² and Y³ which are independent ofone another, is a hydrogen atom, a chlorine atom or a fluorine atom);

(provided that in the formula (a2), R^(a) is a hydrogen atom or a methylgroup, R¹ is a C₁₋₁₂ alkyl group or a C₄₋₁₀ monovalent alicyclic group,j is an integer of from 0 to 8, and k is 0 or 1);

(provided that in the formula (a3), R^(b) is a hydrogen atom or a methylgroup, R² is a C₁₋₁₀ alkylene group or a C₄₋₁₀ bivalent alicyclic group,m is an integer of from 0 to 8, and n is 0 or 1); and

(provided that in the formula (a4), R^(b) and R² are as defined in theformula (a3), respectively, R³ is a C₂₋₁₀ alkylene group or a C₄₋₁₀bivalent alicyclic group, R⁴ is a hydrogen atom or —NHZ¹Z²Z³, whereineach of Z¹, Z² and Z³ which are independent of one another, is ahydrogen atom, a C₁₋₄ alkyl group or a C₁₋₆ hydroxyalkyl group, providedthat at least a part of R⁴ is required to be —NHZ¹Z²Z³, p is an integerof from 0 to 8, and q is 0 or 1).
 2. A process for producing acomposition for aqueous coating material, which comprises: anesterification step of reacting a fluorinated copolymer (B) comprisingfrom 40 to 60 mol % of a structural unit of the formula (a1), from 3 to50 mol % of a structural unit of the formula (a2) and from 4.4 to 37 mol% of a structural unit of the formula (a3) (provided that the total mol% value of the respective structural units of the formulae (a1), (a2)and (a3) is from 80 to 100) with a dibasic acid anhydride in an organicsolvent to esterify a part of the hydroxyl group in the structural unitof the formula (a3) to introduce a carboxyl group; a neutralizing stepof adding a basic compound to neutralize at least a part of the carboxylgroup with the basic compound; a step of adding water; and a step ofremoving the organic solvent:—CFX¹—CX²X³—  Formula (a1) (provided that in the formula (a1), each ofX¹ and X² which are independent of each other, is a hydrogen atom, achlorine atom or a fluorine atom, and X³ is a chlorine atom, a fluorineatom or —CY¹Y²Y³, wherein each of Y¹, Y² and Y³ which are independent ofone another, is a hydrogen atom, a chlorine atom or a fluorine atom);

(provided that in the formula (a2), R^(a) is a hydrogen atom or a methylgroup, R² is a C₁₋₁₂ alkyl group or a C₄₋₁₀ monovalent alicyclic group,j is an integer of from 0 to 8, and k is 0 or 1); and

(provided that in the formula (a3), R^(b) is a hydrogen atom or a methylgroup, R² is a C₁₋₁₀ alkylene group or a C₄₋₁₀ bivalent alicyclic group,m is an integer of from 0 to 8, and n is 0 or 1).
 3. The process forproducing a composition for aqueous coating material according to claim2, wherein the neutralizing step and the step of adding water areconducted at the same time by adding an aqueous solution of the basiccompound.
 4. A two-component curable aqueous coating material kit whichcomprises the composition for aqueous coating material as defined inclaim 1 and a water-soluble or water-dispersible curing agent.
 5. Thecomposition for aqueous coating material according to claim 1, whereinthe structural unit of the formula (a2) is a structural unit whereinj=k=0, and the structural unit of the formula (a3) is a structural unitwherein m=n=0.
 6. The composition for aqueous coating material accordingto claim 1, wherein the organic solvent is at least one member selectedfrom the group consisting of alcohols, cellosolves, propylene glycolderivatives and ketones.
 7. The composition for aqueous coating materialaccording to claim 1, which contains the organic solvent in an amount ofat most 3 mass % in the total mass of the composition for aqueouscoating material.
 8. The composition for aqueous coating materialaccording to claim 1, wherein the content of the structural unit of theformula (a4) in the fluorinated copolymer is from 1.4 to 6 mol %.
 9. Thetwo-component curable aqueous coating material kit according to claim 4,wherein the water-soluble or water-dispersible curing agent is anisocyanate compound.
 10. The two-component curable aqueous coatingmaterial kit according to claim 4, wherein the water-soluble orwater-dispersible curing agent is a non-blocked isocyanate.